| Highlights: |
| |
| » |
Narrow cell banding offers best cell to module wattage realization. |
| » |
100% grading on "Peak Power". |
| » |
100% check on visual appearance. |
| » |
Each cell produced at our facility undergoes a series of thorough quality test. |
|
| |
| Cell Characteristics: General |
| |
| Type of cell |
: |
Mono crystalline |
| Design (Square, Pseudo square) |
: |
Pseudo square |
|
| |
| Cell Characteristics: Mechanical |
| |
| Length |
: |
156.0±0.5 mm |
| Width |
: |
156.0±0.5 mm |
| Dia |
: |
201.0±0.5 mm |
| Accuracy of angles |
: |
90º ± 0.1° |
| Thickness |
: |
* 200 ± 30 µm |
| Maximum bow |
: |
< 1.5 mm |
| Nominal surface area |
: |
238.95 cm² |
| Bus bar width (Front) |
: |
2.0 mm |
| Continuous Pad width (Back) |
: |
2.5 mm |
| Distance between bus bars |
: |
75.0 mm |
|
| |
| Cell Characteristics: Visual |
| |
| A.R. coating |
: |
SiNX |
| Back side surface |
: |
Aluminum |
| Bus bar material front |
: |
Silver |
| Bus bar material back |
: |
Silver continuous pads |
|
| |
| * The cell thickness will change based on the available wafer thickness, |
| |
| |
| Cell Characteristics: Electrical |
| |
| Cells are graded at Peak power with 50 mW banding, the typical wattage bin is given below |
| |
Wattage |
LABEL wattage |
Efficiency % |
From |
To |
|
|
| 4.00 |
< 4.20 |
4.00 |
16.74 |
| 3.95 |
< 4.00 |
3.95 |
16.53 |
| 3.90 |
< 3.95 |
3.90 |
16.32 |
| 3.85 |
< 3.90 |
3.85 |
16.11 |
| 3.80 |
< 3.85 |
3.80 |
15.90 |
| 3.75 |
< 3.80 |
3.75 |
15.69 |
| 3.70 |
< 3.75 |
3.70 |
15.48 |
| 3.65 |
< 3.70 |
3.65 |
15.28 |
| 3.60 |
< 3.65 |
3.60 |
15.07 |
| 3.55 |
< 3.60 |
3.55 |
14.86 |
| 3.50 |
< 3.55 |
3.50 |
14.65 |
| 3.45 |
< 3.50 |
3.45 |
14.44 |
|
| |
|
| |
Note: Parameters specified, are at standard test condition STC, 25°C Ambient, 100 mW/cm 2 irradiance. |
| |
| Parameter |
Specification |
| Shunt Resistivity 1 |
Dark IV Reversed biased:
a) at -10V <10.28mA/cm2 (2.5 A )
*considering cell area as
238.95 cm 2 |
| Polarity |
Front negative, back positive |
| Temperature Coefficient for Voltage |
- 0.32% per deg K |
| Temperature Coefficient for Current |
+ 0.04% per deg K |
| Temperature Coefficient for power |
- 0.42% per deg K |
|
| |
| Packing |
| |
 |
|
 |
| 100 Cells Bunch |
|
400 Cells in one Small Box |
| |
|
|
 |
|
 |
| Master Corrugated Box |
|
Final Master Corrugated Box |
|
| |
| Cell Drawing |
| |
 |
| |
|
| |